新型环保固沙剂的性能研究

doi:10.16039/j.cnki.cn22-1249.2020.01.017

下载:

PDF (444KB)
输出: BibTeX | EndNote (RIS)

摘要

采用木质素磺酸钠、尿素、甲醛和三聚氰胺为主要原料，合成了新型环保固沙剂，为固沙剂领域提供了新品种。采用红外光谱（FT-IR）进行了化学组成分析，测试了固沙试样的抗风蚀性、保水性、抗压强度及耐水性，分析了不同浓度固沙剂的固沙效果。结果表明，新型环保固沙剂能将沙土颗粒紧密粘结，形成较大团聚体结构。喷洒5％的固沙剂的沙模，固沙试样的风蚀率达到0.02％，保水率达到70％左右，抗压强度达到25mm，耐水性达到2.46％，能够满足实际应用要求。

	服务
	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	（）
	作者相关文章
	刘辉
	王玉伟
	邹继颖
	孙大志
	陈立波
	董春欣
	沈士彬
	翦英红
	徐亮亮
	翁士睿

关键词: 化学固沙剂木质素性能测试固沙效果

Abstract:

Using sodium lignin sulfonate, urea, formaldehyde and Melamine as the main raw materials, a new type of environmentally-friendly sand fixing agent was synthesized to provide a new variety of sand fixing agent. The chemical composition analysis was carried out by FT-IR, the wind corrosion resistance, water retention, compressive strength and water resistance of sand fixing samples were measured, and the sand fixing effect of different concentration of sand fixing agents was analyzed. The results show that the new environmentally friendly sand fixation agent can bond the sand particles tightly to form a larger aggregate structure. The sand mold of the sand fixing agent sprayed 5%, the wind erosion rate of the sand fixing specimen reached 0.02 %, the water retention rate reached about 70 %, the compressive strength reached 25mm, and the water resistance reached 2.46 %, which can meet the actual application requirements.

Key words: chemical stabilizers lignin performance testing sand fixing effect

出版日期: 2020-01-25 发布日期: 2020-01-25 整期出版日期: 2020-01-25

ZTFLH:

X43

引用本文:

刘辉, 王玉伟, 邹继颖, 孙大志, 陈立波, 董春欣, 沈士彬, 翦英红, 徐亮亮, 翁士睿. 新型环保固沙剂的性能研究 [J]. 吉林化工学院学报, 2020, 37(1): 77-80.
LIU Hui, WANG Yuwei, ZOU Jiying, SUN Dazhi, ChEN Libo, DONG Chunxin, SHEN Shibin, JIAN Yinghong, XU Liangliang, WENG Shirui. Study on Performance of New Environmental Protection Stabilizer . Journal of Jilin Institute of Chemical Technology, 2020, 37(1): 77-80.

链接本文:

http://xuebao.jlict.edu.cn/CN/10.16039/j.cnki.cn22-1249.2020.01.017 或 http://xuebao.jlict.edu.cn/CN/Y2020/V37/I1/77

[1]	WANG Hui-zhu, WANG Su-fan, DENG Bo-wen, ZHANG Long, CHEN Shuai. Research Progress on Bioactive Components and Product Development of Apocynum Venetum [J]. Journal of Jilin Institute of Chemical Technology, 2018, 35(11): 4 -7 .
[2]	LIN Zong-de. Design of an Intelligent Baby Carriage [J]. Journal of Jilin Institute of Chemical Technology, 2019, 36(1): 36 -42 .
[3]	ZOU Ji-ying, SUN Da-zhi, CHEN Li-bo, DONG Chun-xin, LI Wan-hai, LIU Hui. Research on the Integration of "Internet +" into the Practical Teaching System of Environmental Science Majors [J]. Journal of Jilin Institute of Chemical Technology, 2019, 36(2): 20 -22 .
[4]	BAI Xue, Zhao Liang. Micro Services: Construction of Information Functional Composition Platform based on Enterprise WeChat [J]. Journal of Jilin Institute of Chemical Technology, 2019, 36(3): 59 -61 .
[5]	LIANG Hui. The Effects of Input and Output Task Types on English Learners' Formulaic Sequences [J]. Journal of Jilin Institute of Chemical Technology, 2019, 36(6): 69 -72 .
[6]	ZU Guojing, LU Hehuan, WU Lishun, TONG Qingsong. Preparation and Adsorption Properties of Polyvinyl Alcohol Polyacrylamide Interpenetrating Polymer Network Hydrogel [J]. Journal of Jilin Institute of Chemical Technology, 2020, 37(1): 1 -7 .
[7]	JIN Hua, WANG Guihai, LIU Baojun, REN Dongsheng, WANG Kangjing, WANG Dayue, LIU Rong, YAO Pengbo. Fabrication and photocatalytic properties of Ag₃PO₄/GO photocatalyst [J]. Journal of Jilin Institute of Chemical Technology, 2020, 37(1): 8 -12 .
[8]	. [J]. Journal of Jilin Institute of Chemical Technology, 2019, 36(12): 0 .
[9]	YU Wencui, GAO Mintao. Simultaneous Determination of Four Components in Niuhuangqingwei Pills by HPLC [J]. Journal of Jilin Institute of Chemical Technology, 2020, 37(1): 13 -16 .
[10]	ZENG Xiaodan, MA Mingshuo, JIN Xing. Determination of selenium in Ligusticum chuanxiong by atomic fluoerescence spectrometry [J]. Journal of Jilin Institute of Chemical Technology, 2020, 37(1): 17 -19 .